In vitro study of marginal microleakage levels in restorations with Bulk Fill resins using the deproteinization technique prior to acid etching
DOI:
https://doi.org/10.59334/ROV.v2i43.639Palabras clave:
microfiltración marginal, resinas Bulk , desproteinizaciónResumen
Introduction: Currently, the market offers Bulk Fill resins that are used with the monobloc or single-increment technique (up to 4 or 5 mm). These resins are characterized by a lower filler content and larger filler particles, improved translucency, and a different chemical structure of the monomers in the filler compounds, which—when placed in a single block—reduce polymerization stress. Objective: To evaluate the level of marginal microleakage of two Bulk Fill resins using the deproteinization technique prior to acid etching. Methods: This is an in vitro study in which 64 extracted premolars underwent standardized cavity preparations. The teeth were randomly divided into four groups and subjected to a manual thermocycling process of 500 cycles. All samples were immersed in a 2% methylene blue solution for 24 hours. Microleakage was then observed with a stereomicroscope. Results: For the Aura Bulk Fill resin, microleakage in enamel was observed in 25% of the deproteinized samples and in 18.8% of the non-deproteinized samples. For the Filtek Bulk Fill resin, 31.3% of the samples exhibited microleakage in enamel with the deproteinization technique and 25.0% without deproteinization. No statistically significant differences were found. Conclusions: All samples presented microleakage, with similar levels in both brands of Bulk Fill resins, and no significant differences were observed with the application of the deproteinization technique.
Descargas
Referencias
Baltacioglu, I. H., Demirel, G., Öztürk, B., Aydin, F., & Orhan, K. (2024). Marginal adaptation of bulk-fill resin composites with different viscosities in class II restorations: A micro-CT evaluation. BMC Oral Health, 1(24), 228-228. https://doi.org/10.1186/s12903-024-03975-7
Baracco, B., Fuentes, V., & García, L. C. (2016). Efecto del termociclado y del grabado ácido previo en la resistencia adhesiva al esmalte de distintos adhesivos autograbados. Científica Dental: Revista Científica de Formación Continuada, 13(1), 49–56. https://coem.org.es/pdf/publicaciones/cientifica/vol13num1/49-56.pdf
Behery, H., El-Mowafy, O., El-Badrawy, W., Nabih, S., & Saleh, B. (2018). Gingival microleakage of class II bulk-fill composite resin restorations. Dental and Medical Problems, 55(4), 383–388. https://doi.org/10.17219/dmp/99264
Cáceres, L. M., Núñez, H., & Perdomo, M. (2021). Evaluación de la microfiltración en restauraciones con resina Clase I. Revista Estomatológica Herediana, 31(4), 242-247. https://doi.org/10.20453/reh.v31i4.4091
Cayo, C. F., & Carrillo, A. A. (2020). Sellado marginal aplicando hipoclorito de sodio versus ácido fosfórico como acondicionador dental. Revista Cubana de Estomatología,57(1). http://scielo.sld.cu/scielo.php?script=sci_abstract&pid=S0034-75072020000100008&lng=es&nrm=iso&tlng=es
Cayo, C., Llancari, L., Mendoza, R., & Cervantes, L. (2019). Marginal filling and adhesive resistance of bulk fill resin applying 18% edta gel compared with 37% phosphoric acid gel in vitro dental conditioning. J. Oral Res. (Impresa), 3(8), 228-235. https://doi.org/10.17126/joralres.2019.034
Del Valle, A. M., Del Rosario, N. M., & Christiani, J. J. (2021). Filtración marginal y contracción en la polimerización en nuevas resinas bulk fill: una revisión de la literatura. Rev. Ateneo Argent. Odontol, 64(1), 77-82. https://docs.bvsalud.org/biblioref/2021/06/1252984/articulo12.pdf
Elgendy, H., Maia, R. R., Skiff, F., Denehy, G., & Qian, F. (2019). Comparison of light propagation in dental tissues and nano-filled resin-based composite. Clinical Oral Investigations, 23(1), 423-433. https://doi.org/10.1007/s00784-018-2451-9
Grandon, F., Muster, M., & Wendler, M. (2020). Solving color irregularities with a bioactive bulk-fill restorative system: Case report and 24-months follow up. J. Oral Res. (Impresa), 5(9), 430-436. https://doi.org/10.17126/joralres.2020.086
Khairy, N. M., Elkholany, N. R., & Elembaby, A. E. (2024). Evaluation of surface microhardness and gingival marginal adaptation of three different bulk-fill flowable resin composites: A comparative study. J Esthet Restor Dent, 6(32), 920-929.https://doi.org/10.1111/jerd.13211
Kury, M., Goulart, M., Thomé, T., Conceição, E. N., Coelho-de-Souza, F. H., Cavalli, V., & Erhardt, M. C. G. (2020). Three-year follow-up of flowable bulk-fill resin restorations in posterior teeth: A double-blind randomized controlled clinical trial. Rev. Fac. Odontol. Porto Alegre, 2(16), 50-63. https://doi.org/10.22456/2177-0018.104810
Lang-Salas, M., Villarreal-Romero, L., Domínguez-Monreal, J., Cuevas-González, J., Donohué-Cornejo, A., Reyes-López, S., Zaragoza-Contreras, E., & Espinosa-Cristóbal, L. (2020). Evaluación de la adhesión de sistemas adhesivos de grabado total en esmalte dental bovino usando un agente desproteinizante: un estudio in vitro. Revista de La Asociación Dental Mexicana, 77(1), 22–27. https://doi.org/10.35366/od201e
Larraechea, B., Rodríguez, S., & Toledo, J. (2020). Técnica bulk-fill comparada con técnica incremental para restauraciones posteriores en pacientes con dentición permanente. International journal of interdisciplinary dentistry, 13(3), 196-200. https://doi.org/10.4067/S2452-55882020000300196
Licla, K., & Albites, U. (2015). Grado de microfiltración de un sellante resinoso con diferentes sistemas adhesivos. Revista Odontología Pediátrica, 14(2), 120-128.http://repebis.upch.edu.pe/articulos/op/v14n2/a4.pdf
López, N. A., Munayco, E. R., Torres, G., Blanco, D. J., Siccha, A., & López, R. P. (2019). Deproteinization of primary enamel with sodium hypochlorite before phosphoric acid etching. Acta Odontologica Latinoamericana: AOL, 32(1), 29-35. https://actaodontologicalat.com/wp-content/uploads/2019/06/aol_2019_32_1_29.pdf
López, P. F. (2017). Comparación in vitro de microfiltración entre una resina nanohibrida y una resina bulk en molares con restauración clase I, UAC, Cusco-2017 [tesis]. Universidad Andina del Cusco. https://repositorio.uandina.edu.pe/backend/api/core/bitstreams/a994aff0-a72f-427e-9d13-9c5d57a1e505/content
Lorca, D., Tiffi, C., Sarmiento, R., & Sarmiento, J. (2023). In vitro comparison of marginal infiltration between a conventional resin and a bulk-fill resin, in the relocation of cervical margins technique. J. Oral Res. (Impresa), 1(12), 1-11. https://doi.org/10.17126/joralres.2023.001
Mosharrafian, S., Farahmand, N., Poorzandpoush, K., Hosseinipour, Z. S., & Kahforushan, M. (2023). In vitro microleakage at the enamel and dentin margins of class II cavities of primary molars restored with a bulk-fill and a conventional composite. Clinical and Experimental Dental Research, 9(3), 512-517. https://doi.org/10.1002/cre2.729
Navarrete, J. X. (2018). Microfiltración en la cementación con resina nanohíbrida y Bulk termomodificadas en incrustaciones Inlay en molares, Cusco-2018 [tesis]. Universidad Alas Peruanas. https://repositorio.uap.edu.pe/xmlui/handle/20.500.12990/3619
Porto Gurgel, I. P., Ataíde, M., Azevedo, M. E., & Resende, M. A. J. (2011). Influencia del tiempo de almacenamiento en la resistencia de unión a la dentina desproteinizada, utilizando tres diferentes adhesivos dentales. Acta Odontológica Venezolana, 49(4). https://www.actaodontologica.com/ediciones/2011/4/art-10/
Rodríguez, A. M. del V., Christiani, J. J., Alvarez, N., & Zamudio, M. E. (2018). Revisión de resinas Bulk Fill: Estado actual. Rev. Ateneo Argent. Odontol, 1(58), 55-60. https://www.ateneo-odontologia.org.ar/articulos/lviii01/articulo6.pdf
Rojas, S. V., & Ríos, T. E. (2021). Microfiltración marginal de resinas de relleno masivo y nanohíbrida en molares deciduos. Revista Cubana de Estomatología, 58(2).http://scielo.sld.cu/scielo.php?script=sci_abstract&pid=S0034-75072021000200007&lng=es&nrm=iso&tlng=es
Roque, J. G., Zavala, N. V., Patiño, N., & Martínez, G. A. (2021). Effect of sodium hypochlorite in ground fluorotic enamel: Shear bond strength and surface analysis. Odovtos International Journal of Dental Sciences, 23(3), 107-119. https://doi.org/10.15517/ijds.2021.47574
Sampaio, C. S., Abreu, J. L. B. de, Kornfeld, B., Silva, E. M. da, Giannini, M., & Hirata, R. (2024). Short curing time bulk fill composite systems: Volumetric shrinkage, degree of conversion and Vickers hardness. Brazilian Oral Research, 1(38), e030. https://doi.org/10.1590/1807-3107bor-2024.vol38.0030
Zheng, B., Cao, S., Al-Somairi, M. A. A., He, J., & Liu, Y. (2022). Effect of enamel-surface modifications on shear bond strength using different adhesive materials. BMC Oral Health, 22(1), 222-224. https://doi.org/10.1186/s12903-022-02254-7
Publicado
Licencia
Derechos de autor 2024 Herbert Cosio Dueñas

Esta obra está bajo una licencia internacional Creative Commons Atribución 4.0.
Los autores que publican con Odontologia Vital aceptan los siguientes términos:
- Los autores conservan los derechos de autor sobre la obra y otorgan a la Universidad Latina de Costa Rica el derecho a la primera publicación, con la obra reigstrada bajo la licencia Creative Commons de Atribución/Reconocimiento 4.0 Internacional, que permite a terceros utilizar lo publicado siempre que mencionen la autoría del trabajo y a la primera publicación en esta revista.
- Los autores pueden llegar a acuerdos contractuales adicionales por separado para la distribución no exclusiva de la versión publicada del trabajo de Odontología Vital (por ejemplo, publicarlo en un repositorio institucional o publicarlo en un libro), con un reconocimiento de su publicación inicial en Odontología Vital.
- Se permite y recomienda a los autores/as a compartir su trabajo en línea (por ejemplo: en repositorios institucionales o páginas web personales) antes y durante el proceso de envío del manuscrito, ya que puede conducir a intercambios productivos, a una mayor y más rápida citación del trabajo publicado.